Iron Powders

Chemical Composition Analysis

IRON POWDER AT 40:29
Type Minimum Maximum
Mn - 0.20%
Si - 0.10%
H2 Loss - 0.50%
V - 0.10%
C - 0.03%
S - 0.03%
P - 0.03%
O-TOTAL - 0.50%
Fe Balance -


Minimum Maximum
APPARENT DENSITY (G/CM3) 2.80 3.20


ASTM MICRONS RETENTIONS
+35 +500 0.00% Min
-35+40 -500+420 10.00% Max
-40+100 -420+150 30.00% -70.00%
-100+200 -150+75 20.00% Max
-325 - 45 10.00% Max


IRON POWDER AT 40.37
Type Minimum Maximum
Mn - 0.20%
Si - 0.10%
H2 Loss - 0.50%
V - 0.10%
C - 0.05%
S - 0.03%
P - 0.03%
O-TOTAL - 0.50%
Fe Balance -


Minimum Maximum
APPARENT DENSITY (G/CM3) 3.60 3.80


ASTM MICRONS RETENTIONS
+35 +500 0.00% Min
-35+40 -500+420 10.00% Max
-40+100 -420+150 30.00% -70.00%
-100+200 -150+75 20.00% Max
-325 - 45 10.00% Max


IRON POWDER AT 100.25
Type Minimum Maximum
Mn - 0.20%
Si - 0.10%
H2 Loss - 0.50%
V - 0.10%
C - 0.03%
S - 0.03%
P - 0.03%
O-TOTAL - 0.50%
Fe Balance -


Minimum Maximum
APPARENT DENSITY (G/CM3) 2.30 2.50


ASTM MICRONS RETENTIONS
+80 +180 5.00% Max
-80+100 -180+150 10.00% Max
+100+325 -150+45 Balance
-325 -45 30.00% Max


IRON POWDER AT 100.29
Type Minimum Maximum
Mn - 0.20%
Si - 0.10%
H2 Loss - 0.50%
V - 0.10%
C - 0.03%
S - 0.03%
P - 0.03%
O-TOTAL - 0.50%
Fe Balance -


Minimum Maximum
APPARENT DENSITY (G/CM3) 2.80 3.00


ASTM MICRONS RETENTIONS
+80 +180 5.00% Max
-80+100 -180+150 10.00% Max
+100+325 -150+45 Balance
-325 -45 30.00% Max